铁路钢桥高强度紧固螺栓断裂分析及防护

doi:10.3976/j.issn.1002-4026.2023.02.009

Abstract

Abstract:

Several high-strength fastening bolts were found broken on a railway steel bridge. Failure analysis of these bolts was performed to determine why they fractured and to prevent future bolt fractures. The fracture morphology, microarea-chemical analysis of the fracture, microstructure and hardness of the bolts, compositional contents, and mechanical properties of the bolt steel were analyzed by using scanning electron microscopy, energy dispersive X-ray spectrometry, optical microscopy, a Rockwell hardness tester, X-ray fluorescence spectrometry, and an electronic universal testing machine, respectively. The results indicate that the compositional contents, hardness, and mechanical properties are consistent with the 20MnTiB steel standard. In addition, dendritic cracks can be observed in the fracture initiation zones of the fastening bolts and the corrosion products in the cracks contain sulfur.The fastening bolts are subjected to cyclic loads in normal working conditions. Therefore, fractures of the fastening bolts were caused by corrosion fatigue fractures under cyclic loads. The cracks initiated at the root of the screw thread or the connecting point between the stud and nut, which are particularly vulnerable to stress corrosion cracks caused by the presence of sulfur.

Key words: steel bridge, high strength bolt, stress corrosion crack, fatigue, fracture

CLC Number:

TG115

GUO Weimin, DONG Youfu, LEI Tai'an, ZHANG Qinran, LIU Guoqiang, LIU Guofei, MENG Lingqiang, TIAN Linan, DING Ning. Fracture analysis and prevention of high-strength fastening bolts used in railway steel bridges[J].Shandong Science, 2023, 36(2): 69-75.

Figures/Tables 12

Fig.1

Fig.2

Table 1

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Table 2

Table 3

References 10

[1]	周远棣, 徐君兰. 钢桥[M]. 北京: 人民交通出版社, 1991.
[2]	中铁九桥工程有队公司. 公路桥梁施工系列手册:桥梁钢结构[M]. 北京: 人民交通出版社, 2014.
[3]	刘楠. 普速铁路桥梁检定评估实践与研究[M]. 北京: 中国铁道出版社, 2015.
[4]	方秦汉, 高宗余, 李加武. 中国铁路钢桥的发展历程及展望[J]. 建筑科学与工程学报, 2008, 25(4): 1-5.
[5]	刘宏刚, 张洪玉, 彭月燊. 铁路钢桥高强度螺栓连接施工若干问题探讨[J]. 铁道标准设计, 2015, 59(2): 60-64. DOI:10.13238/j.issn.1004-2954.2015.02.015. doi: 10.13238/j.issn.1004-2954.2015.02.015
[6]	程军. 钢桥的腐蚀及其防护措施探析[J]. 铁道建筑, 2008 (7): 21-23.
[7]	林浩. 浅谈钢桥防腐的研究概况[J]. 山西交通科技, 2016(4): 83-84.
[8]	陶晓燕, 张玉玲. 铁路钢桥结构疲劳极限状态设计方法研究[J]. 铁道工程学报, 2014, 31(5): 59-62.
[9]	国家钢铁工业协会. 合金结构钢:GB/T 3077—2015[S]. 北京: 中国标准出版社, 2015.
[10]	中国机械工业联合会. 钢结构用高强度大六角头螺栓、大六角螺母、垫圈技术条件:GB/T 1231—2006[S]. 北京: 中国标准出版社, 2006.

Metrics

Comments

Recommended 0

Open Access This article is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License (CC BY-NC 4.0), which permits third parties to freely share (i.e., copy and redistribute the material in any medium or format) and adapt (i.e., remix, transform, or build upon the material) the articles published in this journal, provided that appropriate credit is given, a link to the license is provided, and any changes made are indicated. The material may not be used for commercial purposes. For details of the CC BY-NC 4.0 license, please visit: https://creativecommons.org/licenses/by-nc/4.0

项目	w(C)	w(Si)	w(Mn)	w(P)	w(S)	w(Ti)	w(Cr)	w(Ni)	w(Mo)	w(Fe)
断裂螺栓	0.22	0.22	1.41	0.015	0.013	0.048	<0.010	0.024	<0.010	Bal.
GB/T 3077—2015(20MnTiB)	0.17~0.24	0.17~0.37	1.30~1.60	≤0.030	≤0.030	0.04~0.10	≤0.30	≤0.30	≤0.10	Bal.

项目	抗拉强度/MPa	冲击吸收能量/J
断裂螺栓	1 116	63.7
GB/T 1231—2006(10.9S级20MnTiB)	1 040~1 240	≥47

测试部位	洛氏硬度(HRC)	平均值(HRC)
断口横截面	37.5 36.1 36.0	36.5
断口纵截面	37.0 37.3 37.1	37.1
GB/T 1231—2006(10.9S级20MnTiB)	33≤洛氏硬度≤39

[1]	ZHANG Shumin, WANG Xiaoping, TIAN Jing, XU Huixia, LIU Long, DING Ning. Fracture analysis of copper nuts in the three-position mechanism of ultra-high voltage circuit breakers [J]. Shandong Science, 2025, 38(5): 56-63.
[2]	ZENG Ting, YANG Ran, LI Qingjun, GONG Yanan, WANG Shuzhen, LIU Qian. Effects of Dioscorea opposita Thunb. polysacchariades on exercise-related fatigue in mice through the PI3K/AKT/Gsk-3β pathway [J]. Shandong Science, 2024, 37(6): 51-58.
[3]	WANG Xiaoyang, WAN Chenguang, WANG Xiaofeng. Prediction of mechanical properties of asphalt mixtures based on optimized neural networks [J]. Shandong Science, 2024, 37(4): 56-64.
[4]	LI Hui-rong , LI Zhi. Analysis of fatigue fracture failure mechanism of a coated steel roller of LT1350 coating line [J]. Shandong Science, 2020, 33(3): 82-86.
[5]	CHEN Yan-fei, SONG Xiao-cun, LAI Hua-sheng, WEN Xiao-qiang, ZHOU Ji-xue. Fracture failure analysis and process improvement of iron-based powder metallurgy gears [J]. Shandong Science, 2020, 33(2): 27-32.
[6]	LIU Long, JIANG Ting, HOU Nan, ZHANG Zong-yang, DING Ning. The reconstruction method for fracture surface morphology of metal parts based on 3D technologies [J]. Shandong Science, 2019, 32(3): 42-47.
[7]	LI Jin-hua, BAI De-qian, LIU Tie-sheng. Fatigue reliability analysis of pressure shell structure for manned submersible [J]. Shandong Science, 2019, 32(2): 34-41.
[8]	XIU Da-peng,ZHANG Su-qing,ZHOU Ji-xue，YANG Yuan-sheng，HAN Qing-you. Failure analysis for abnormal fracture of nodular cast iron QT500-7 air compressor shaft [J]. SHANDONG SCIENCE, 2017, 30(6): 41-44.
[9]	LIU Shu-hua, WANG Xiao, ZHANG Jian-wei. The critical angle which enables the formation of a new fracture and its relation with strong earthquake [J]. SHANDONG SCIENCE, 2017, 30(1): 98-102.
[10]	XIU Dapeng，ZHANG Xinen. Failure analysis of facade plate fracture of gas generator [J]. SHANDONG SCIENCE, 2016, 29(2): 36-40.
[11]	XU Na, LI En-Xia, SHI Jun-Bo, GUO Wei-Min, MA Hong, LI Yong-De. Failure analysis of early fracture of the combination rib in a change wheel of ADC14 aluminium alloy [J]. J4, 2012, 25(4): 36-39.
[12]	PENG Wei-Bing, HE Qiu-Xia, LIU Ke-Chun, CHEN Xi-Qiang. Experimental research on anti-fatigue efficacy of peanut peptides in mice [J]. J4, 2011, 24(5): 35-38.

Fracture analysis and prevention of high-strength fastening bolts used in railway steel bridges

RichHTML

PDF (PC)

Like

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 12

References 10

Related Articles 12

Metrics

Comments

Recommended 0