热处理对TiAl基合金喷丸试样组织与性能的影响

doi:10.3976/j.issn.1002-4026.2023.02.008

摘要/Abstract

摘要：

TiAl合金在高温下服役时,表面因受循环载荷而容易产生疲劳裂纹,因此有必要进行表面处理以改善其力学性能。使用直径0.2 mm钢丸在0.7 MPa气压下对TiAl合金进行室温喷丸实验,使用ABAQUS有限元分析软件进行喷丸仿真模拟研究。随后,对喷丸试样进行不同温度和保温时间的热处理。通过SEM观察TiAl合金纵截面的显微组织,使用X射线残余应力仪测量TiAl合金表面的残余压应力,使用显微硬度仪测量热处理后TiAl合金表面的显微硬度。结果发现,喷丸后TiAl合金表面出现许多凹坑和层片状突起,次表面处发生明显塑性变形并出现许多变形孪晶。热处理后TiAl合金表面残余压应力会随着保温时间的增加和热处理温度的升高而变小。硬度几乎表现出与残余应力相同的趋势,但当热处理温度为1 200 ℃时,因金相组织发生变化,α₂相含量明显增多,导致硬度增加。

关键词: TiAl合金, 喷丸, 热处理, 有限元模拟

Abstract:

Because TiAl alloys are susceptible to fatigue cracking on their surfaces due to cyclic loading when used at high temperatures, it is necessary to treat their surfaces to improve their mechanical properties. In this study, TiAl alloy was subjected to shot peening tests at room temperature, using 0.2 mm diameter steel shots at 0.7 MPa air pressure. The shot peening simulation studies were conducted using ABAQUS finite element analysis software. Subsequently, the shot-peened specimens were heat treated at different temperatures and holding times. The cross-sectional microstructures of the specimens were observed using a scanning electron microscope (SEM), the residual compressive stresses on the surfaces were measured using an X-ray residual stress meter, and the surface microhardness after heat treatment was measured using a microhardness meter. The results showed that many pits and lamellar protrusions appeared on the surface of TiAl alloy after shot peening, and obvious plastic deformations and numerous deformation twins appeared at the secondary surface. The residual compressive stress on the surface of the TiAl alloy after heat treatment decreased as the holding time and heat treatment temperature increased. Hardness followed a similar trend as the residual stress; however, when the heat treatment temperature was raised to 1 200 ℃, the hardness increased due to the change of metallographic organization and a significant increase inα₂ phase content.

Key words: TiAl alloy, shot peening, heat treatment, finite element simulation

中图分类号:

TG146.2

刘立华, 温道胜, 王守仁, 牛金涛, 宋强, 殷子强. 热处理对TiAl基合金喷丸试样组织与性能的影响[J]. 山东科学, 2023, 36(2): 59-68.

LIU Lihua, WEN Daosheng, WANG Shouren, NIU Jintao, SONG Qiang, YIN Ziqiang. Effect of heat treatment on the organization and properties of TiAl-based alloy shot-peened specimens[J]. Shandong Science, 2023, 36(2): 59-68.

图/表 13

表1

图1

图2

图3

图4

图5

图6

图7

图8

图9

图10

图11

图12

参考文献 28

[1]	WEN D S, KONG B B, WANG S R, et al. Mechanism of hydrogen-restrained crack propagation and practical application research of thermohydrogen treatment in a TiAl-based alloy[J]. International Journal of Hydrogen Energy, 2019, 44(13): 6938-6948. DOI:10.1016/j.ijhydene.2019.01.177. doi: 10.1016/j.ijhydene.2019.01.177
[2]	WEN D S, KONG B B, WANG S R, et al. Atomic-scale investigation on fretting wear mechanism of γ phase in a cast Ti-45Al alloy[J]. Applied Surface Science, 2021, 565: 150555. DOI:10.1016/j.apsusc.2021.150555. doi: 10.1016/j.apsusc.2021.150555
[3]	WEN D S, ZONG YY, XU W C, et al. The effect of hydrogen on phase transformation and mechanical properties of a β containing γ-TiAl based alloy[J]. International Journal of Hydrogen Energy, 2014, 39(30): 17404-17415. DOI:10.1016/j.ijhydene.2014.08.051. doi: 10.1016/j.ijhydene.2014.08.051
[4]	WEN D S, ZONG YY, WANG Y Q, et al. Positive influence of hydrogen on the hot workability and dynamic recrystallization of a γ-TiAl based alloy[J]. Materials Science and Engineering: A, 2016, 656: 151-164. DOI:10.1016/j.msea.2016.01.001. doi: 10.1016/j.msea.2016.01.001
[5]	温道胜, 宗影影, 徐文臣, 等. 0.037%H对铸态Ti-45A1-5Nb-0.8Mo-0.3Y合金高温变形行为的影响[J]. 金属学报, 2013, 49(11): 1428-1432. doi: 10.3724/SP.J.1037.2013.00507
[6]	宗影影, 温道胜, 邵斌, 等. 0.2%H对Ti2AlNb基合金板材高温拉伸变形行为的影响[J]. 材料研究学报, 2014, 28(4): 248-254.
[7]	赵波, 姜燕, 别文博. 超声滚压技术在表面强化中的研究与应用进展[J]. 航空学报, 2020, 41(10): 023685.
[8]	TONG Z P, REN X D, ZHOU W F, et al. Effect of laser shock peening on wear behaviors of TC11 alloy at elevated temperature[J]. Optics & Laser Technology, 2019, 109: 139-148. DOI:10.1016/j.optlastec.2018.07.070. doi: 10.1016/j.optlastec.2018.07.070
[9]	YAN H Z, ZHU P F, CHEN Z, et al. Effect of shot peening on the surface properties and wear behavior of heavy-duty-axle gear steels[J]. Journal of Materials Research and Technology, 2022, 17: 22-32. DOI:10.1016/j.jmrt.2021.12.126. doi: 10.1016/j.jmrt.2021.12.126
[10]	RAI A K, BISWAL R, GUPTA R K, et al. Enhancement of oxidation resistance of modified P91 grade ferritic-martensitic steel by surface modification using laser shock peening[J]. Applied Surface Science, 2019, 495: 143611. DOI:10.1016/j.apsusc.2019.143611. doi: 10.1016/j.apsusc.2019.143611
[11]	ZHU L H, GUAN Y J, WANG Y J, et al. Influence of process parameters of ultrasonic shot peening on surface roughness and hydrophilicity of pure titanium[J]. Surface and Coatings Technology, 2017, 317: 38-53. DOI:10.1016/j.surfcoat.2017.03.044. doi: 10.1016/j.surfcoat.2017.03.044
[12]	ZHAO C M, GAO Y K, GUO J, et al. Investigation on residual stress induced by shot peening[J]. Journal of Materials Engineering and Performance, 2015, 24(3): 1340-1346. DOI:10.1007/s11665-014-1382-0. doi: 10.1007/s11665-014-1382-0
[13]	KUMAR P, MAHOBIA G S, CHATTOPADHYAY K. Surfacenanocrystallization of β-titanium alloy by ultrasonic shot peening[J]. Materials Today: Proceedings, 2020, 28: 486-490. DOI:10.1016/j.matpr.2019.10.174. doi: 10.1016/j.matpr.2019.10.174
[14]	LINDEMANN J, BUQUE C, APPEL F. Effect of shot peening on fatigue performance of a lamellar titaniumaluminidealloy[J]. ActaMaterialia, 2006, 54(4): 1155-1164. DOI:10.1016/j.actamat.2005.10.043. doi: 10.1016/j.actamat.2005.10.043
[15]	QIAO H C, ZHAO J B, ZHANG G X, et al. Effects of laser shock peening on microstructure and residual stress evolution in Ti-45Al-2Cr-2Nb-0.2B alloy[J]. Surface and Coatings Technology, 2015, 276: 145-151. DOI:10.1016/j.surfcoat.2015.06.065. doi: 10.1016/j.surfcoat.2015.06.065
[16]	QIAO H C, ZHAO J B, GAO Y. Experimental investigation of laser peening onTiAl alloy microstructure and properties[J]. Chinese Journal of Aeronautics, 2015, 28(2): 609-616. DOI:10.1016/j.cja.2015.01.006. doi: 10.1016/j.cja.2015.01.006
[17]	HUANG Z W, LIN J P, ZHAO Z X, et al. Fatigue response of a grain refined TiAl alloy Ti-44Al-5Nb-1W-1B with varied surface quality and thermal exposure history[J]. Intermetallics, 2017, 85: 1-14. DOI:10.1016/j.intermet.2017.01.010. doi: 10.1016/j.intermet.2017.01.010
[18]	HUANG Z W, SUN C. On the role of thermal exposure on the stress controlled fatigue behaviour of a high strength titanium-aluminum alloy[J]. Materials Science and Engineering: A, 2014, 615: 29-41. DOI:10.1016/j.msea.2014.07.063. doi: 10.1016/j.msea.2014.07.063
[19]	ZHAO W Y, LIU Y Z, LIU L, et al. Surface recrystallization of a gamma-TiAl alloy induced by shot peening and subsequent annealing treatments[J]. Applied Surface Science, 2013, 270: 690-696. DOI:10.1016/j.apsusc.2013.01.129. doi: 10.1016/j.apsusc.2013.01.129
[20]	FANG L, LIN J P, LIANG Y F, et al. Microstructural instability in surface layer of a high Nb-TiAl alloy processed by shot peening following high temperature exposure[J]. Intermetallics, 2016, 78: 8-16. DOI:10.1016/j.intermet.2016.08.004. doi: 10.1016/j.intermet.2016.08.004
[21]	陈海宽, 徐广涛, 孙博, 等. 喷丸对18CrNiMo7-6钢硬度影响的有限元分析[J]. 机械强度, 2022, 44(3): 726-730. DOI:10.16579/j.issn.1001.9669.2022.03.030. doi: 10.16579/j.issn.1001.9669.2022.03.030
[22]	WU L H, JIANG C H. Investigation on surface layers characteristics of pre-stressed shot peeninginconel 625[J]. Materials Transactions, 2019, 60(12): 2558-2561. DOI:10.2320/matertrans.mt-m2019106. doi: 10.2320/matertrans.mt-m2019106
[23]	THOMAS M, LINDLEY T, RUGG D, et al. The effect of shot peening on the microstructure and properties of a near-alpha titanium alloy following high temperature exposure[J]. Acta Materialia, 2012, 60(13/14): 5040-5048. DOI:10.1016/j.actamat.2012.06.017. doi: 10.1016/j.actamat.2012.06.017
[24]	KLEMENZ M. Anwendung der Simulation der Randschichtausbildung beim Kugelstrahlen aufdie Abschätzung der Schwingfestigkeit gekerbter Bauteile[D]. Baden-Wertenburg, Germany: Karlsruhe Institute of Technology, 2009.
[25]	段冰冰, 王治国, 蔡晋, 等. 钛合金表面纳米化强化研究进展[J]. 表面技术, 2021, 50(12): 202-216. DOI:10.16490/j.cnki.issn.1001-3660.2021.12.021. doi: 10.16490/j.cnki.issn.1001-3660.2021.12.021
[26]	INUI H, OH M H, NAKAMURA A, et al. Ordered domains intial coexisting with ti3al in the lamellar structure of ti-rich tialcompounds[J]. Philosophical Magazine A, 1992, 66(4): 539-555. DOI:10.1080/01418619208201574. doi: 10.1080/01418619208201574
[27]	乔红超, 赵亦翔, 赵吉宾, 等. 激光冲击强化对TiAl合金组织和性能的影响[J]. 光学精密工程, 2014, 22(7): 1766-1773.
[28]	BESCHLIESSER M, CLEMENS H, KESTLER H, et al. Phase stability of a γ-TiAl based alloy upon annealing: Comparison between experiment and thermodynamic calculations[J]. Scripta Materialia, 2003, 49(4): 279-284. DOI:10.1016/S1359-6462(3)00293-8. doi: 10.1016/S1359-6462(3)00293-8

	密度/ (kg·m^-3)	弹性模量/ GPa	泊松比
TiAl合金	4 050	110	0.31
丸粒	7 800	208	0.30